Toray MicroPly™ TCF4050 core splice adhesive is a cyanate ester-based core splice with flatwise tensile strength up to 260°C (500°F). This product has been developed to be compatible with Toray’s high temperature TC420 prepreg resin systems.

Toray MicroPly™ TCF4001 cyanate ester syntactic foam is unique in the industry due to its extremely low density and good structural properties. It does not require pressure during cure to achieve it mechanical properties and can be machined to shape.

Toray MicroPly™ TC4015 cyanate ester film adhesive, formulated for low moisture absorption and high temperature bond strength applications. Its strength and toughness when bonding is often greater than epoxy and polyimides especially at high temperatures.

Toray MicroPly™ SF-5 is a cyanate ester based syntactic film with compatibility to various cyanate ester matrices, including troray RS-3. It is available in unsupported and supported continuous film form in thicknesses from 0.25–6.35 mm (10–250 mils).

Toray MicroPly™ RS-4A is a cyanate ester based film adhesive developed to provide good adhesive performance for core / face skin structures, co-curing and secondary bonding.

Toray MicroPly™ EX-1543 cyanate ester film adhesive formulated for low moisture absorption and/or low dielectric constant and loss applications. It provides strength and toughness when bonding solid, honeycomb or foam core structures at high temperatures.

Toray MicroPly™ EX-1541 cyanate ester syntactic foam is unique due to its extremely low density and good structural properties. It does not require pressure during cure to achieve it mechanical properties and is easily machined to shape if required.

Toray MicroPly™ EX-1516 cyanate ester film adhesive which has been formulated for low moisture absorption and / or low dielectric constant and loss applications. It provides strength and toughness when bonding solid, honeycomb or foam core structures.

Toray MicroPly™ EM-5A is an expanding cyanate ester syntactic film (core splice). Its' unexpanded density is approximately 0.80 g/cc (50 pcf) and it exhibits an expansion ratio of up to 4 times. It is available in continuous film rolls or in sheet form.

TC420 is a flow controlled cyanate ester prepreg, toughened to resist microcracking. TC420 is ideal for out of autoclave large structures in ultra high temperature applications. It is easy to process and yields a low void content under vacuum bag only.

TC410 cyanate ester prepreg achieves extremely low moisture absorption and high conversion levels. TC410 is designed specifically for radomes and satellite structures, providing good resistance to radiation, low microcracking and, low dielectric and loss.

RS-3 is a modified cyanate ester prepreg, providing a good balance between toughness and high temperature/wet performance. RS-3 is qualified in satellite, airframe/missile and, radome structures. RS-3C is a controlled flow vacuum bag only cure version.

RS-16 is a two-part low viscosity cyanate ester RTM resin for wet winding, RTM and VARTM processing. RS-16 is intended for lower temperature exposure and is an ideal system when used with different materials limiting the upper cure temperature.

EX-1545 is a toughened two-part cyanate ester resin with extremely low viscosity at room temperature, allowing RTM to take place with minimal resin heating. This facilitates mold filling time for difficult and / or large RTM’d structures and reduces waste.

EX-1515 cyanate ester prepreg provides optimal mechanical properties, high radiation resistance, microcracking resistance, low moisture absorption / low outgassing while retaining toughness, a low 244°F (118°C) stress-free temperature and long out time.

EX-1510 is a toughened two-part cyanate ester resin with extremely low viscosity at room temperature, allowing RTM to take place without heating the resin. This facilitates mold filling time for difficult and / or large RTM’d structures and reduces waste.

BTCy-2 is our lowest dielectric cyanate ester prepreg resin system. This resin system is valued in high-energy microwave applications due to the low loss tangent.

BTCy-1A is a toughened cyanate ester prepreg. BTCy-1A’s straight-up, easy processing at 177°C (350°F) under low pressure, reduces curing time and production costs, while the system’s negligible volatile emission upon cure allows low void laminates.

BTCy-1 is a 177°C (350°F) curing cyanate ester prepreg and is an industry standard for use on satellite structures and radomes.