Toray MicroPly™ TCF4045 is a low-density epoxy syntactic film. It displays both good mechanical and low dielectric loss and constant properties. The material's base resin chemistry features low moisture absorption with good high temperature properties.

Toray MicroPly™ TCF4035 is a syntactic epoxy film compatible with 121°C (250°F) prepregs. It features a long out time and is offered in a density of approximately 0.6 g/cc (40 ± 4 pounds per cubic foot).

Toray MicroPly™ TC310 is a toughened epoxy film adhesive with excellent mechanical properties and toughness. It is ideal for honeycomb or laminate bonding and may be cured in either autoclave or vacuum bag processing.

Toray MicroPly™ TC263 is a toughened, high peel strength, structural epoxy film adhesive for honeycomb core and laminate bonding. It may be used in low pressure vacuum only, out-of-autoclave processes or in autoclave processes at 15 psi.

Toray MicroPly™ TC235SF-1 is an epoxy composite surfacing film, allowing a smooth, paintable surface from tooling or, a thin-skinned honeycomb stiffened composite structure. It may be cured under vacuum only pressure or under low autoclave pressure.

Toray MicroPly™ RS-15H is an epoxy film adhesive highly flexible with respect to processing. It is compatible with the Toray RS-1 family of prepregs, with all types of reinforcements and cores. It is also suitable for secondary bonding.

Toray MicroPly™ EM-3 is a 121°C (250°F) curing expanding epoxy film of controlled thickness, based on low density syntactic film technology. It is an effective material in generating internal pressure in a closed mold application.

Toray Cetex® TC915 is a thermoplastic composite using a high-performance polyamide matrix resin. This product provides exceptional mechanical properties higher than typical polyamide-based composites and Nylon materials.

Toray Cetex® TC910 is a high strength thermoplastic composite using a polyamide 6 (PA6) matrix resin designed for applications such as automotive and transportation. It provides good heat distortion temperatures and excellent solvent resistance.

Toray Cetex® TC1320 is an engineered thermoplastic composite, utilizing a semi-crystalline polyetherketoneketone resin for outstanding toughness and excellent fire performance.

Toray Cetex® TC1225 is an engineered thermoplastic composite material, utilizing a semi-crystalline engineered polyarlyetherketone resin for excellent mechanical performance and lower processing temperatures.

Toray Cetex® TC1200 is a semi-crystalline polyetheretherketone thermoplastic composite, offering excellent resistance to chemicals and solvents. It is flame retardant and combines outstanding toughness with high temperature performance.

Toray Cetex® TC1130 is a high-end thermoplastic composite, utilizing the amorphous PolyEtherSulphone (PESU) polymer for outstanding toughness and an inherently outstanding fire, smoke, and toxicity performance (< 15/15 OSU).

Toray Cetex® TC1100 is a high-end but cost-effective thermoplastic composite material, utilizing a PPS polymer for excellent mechanical properties and an outstanding chemical and solvent resistance. Qualified for structural application at airframe OEMs.

Toray Cetex® TC1000 Premium is an high-end thermoplastic composite, utilizing the amorphous PEI polymer for outstanding toughness and an inherently outstanding FST performance. Qualified at OEMs for use in aircraft interior and secondary structures.

Toray Cetex® MC1200 PEEK is a thermoplastic BMC based upon TC1200 UD tape using high strength fibers in lengths of up to 25.4mm (1"). MC1200 allows complex shapes to be made with varying wall thickness, integrated ribs and reinforcing structures.

Toray Cetex® MC1100 PPS is a thermoplastic BMC based on TC1100 UD tape using high strength fibers in lengths of up to 25.4mm (1 inch). MC1100 also allows complex shapes to be made with varying wall thickness, integrated ribs and reinforcing structures.

Toray AmberTool® HX56 is an epoxy composite tooling prepreg. After a suitable post cure, an end use temperature of 180ºC (356ºF) is achieved. Toray AmberTool® HX56 achieves an excellent surface finish for small to medium sized autoclave tooling.

Toray AmberTool® HX42 is an epoxy composite tooling prepreg. After a suitable post cure, an end use temperature of 210°C (410°F) is achieved. Toray AmberTool® HX42 has proven pedigree in aerospace tooling.

TC380 is a toughened epoxy prepreg, balanced with excellent OHC, OHT, CAI, and GIC/GIIC properties, low moisture absorption and outstanding hot/wet retention. TC380 is optimized to facilitate the construction of large or complex composite assemblies.

Toray’s TC250 offers an excellent balance of toughness, mechanical properties, and hot/wet performance. It is easily processed via low pressure vacuum bag/oven or under autoclave. TC250 can be post cured for a higher dry and wet Tg.

MS-4H is carbon fiber / epoxy resin compression molding system using high strength, standard modulus (HS) carbon fiber. MS-4H is an excellent low cost, high performance BMC and processes very well in medium to large heavy parts.

E732 is a snap cure toughened epoxy resin matrix optimized for press curing (compression molding) prepreg applications. With a cure time of 4 minutes at 160°C (320°F), an onset Tg of 170°C (338°F) is achieved.

BT250E-6 resin system is a 121°C (250°F) cure epoxy with excellent strength and stiffness. It provides an outstanding surface finish under vacuum bag/oven cure. BT250E-6 has an FAA-accepted database on carbon IM-7 UD tape, S2-glass, and AS-4C plain weave.

BT250E-1 is a 121°C (250°F) cure epoxy prepreg with excellent toughness and strength. It provides an outstanding surface finish with VBO. BT250E-1 is self-adhesive to honeycomb and foam core and, is MIL-R-9300 qualified.